On the thermal characteristics of Mg based composites

The thermal diffusivity, thermal conductivity and thermal expansion were measured to obtaine the information about the behaviour of Mg composites during their heating. The thermal diffusivity indicates precipitation of the [beta]-phase (Mg17Al12) in AZ91 alloy and in AZ91 26 vol.% Saffil fibres composite. The thermal conductivity of QE22 alloy and reinforced QE22 alloy with 10,15 and 25 vol.% SiC particles was obtained in the temperature range of 20--300°C. The thermal conductivity decreases with increasing concentration of the particles and increasing temeperature. The thermal expansion of Mg-30 vol.% Saffil fibres composite was measured and the results were analysed to obtaine information about the residual and thermal strain.

---

Przedstawiono wyniki badań dyfuzyjności, przewodności oraz rozszerzalności cieplnej kompozytów wytworzonych na osnowie stopu AZ91 i QE22 umacnianych cząstkami SiC oraz włóknami Saffil (Al2O3). Badania prowadzono w celu uzyskania informacji o zachowaniu się kompozytów magnezowych podczas ich nagrzewania. Analizy wyników badań dyfuzyjności cieplnej wykazały wydzielanie fazy [beta] (Mg17Al12) zarówno w stopie AZ91, jak i w kompozycie AZ91-26% obj. włókien Al2O3. Badania przewodności cieplnej samego stopu QE22 oraz kompozytu umacnianego 10,15 i 25% obj. cząstek SiC przeprowadzono w zakresie temperatur 20--300°C. Ujawniono, że przewodność cieplna kompozytów malała wraz ze wzrostem udziału objętościowego cząstek oraz ze wzrostem temperatury. Badania rozszerzalności cieplnej kompozytu Mg-30% obj. włókien Saffil pozwoliły natomiast na analizy dostarczające informacji o naprężeniach cząstkowych i cieplnych materiału.