Preparation and characterization of silver sulfathiazole-epoxy resin networks

A new synthetic material was prepared starting from silver sulfathiazole compound and Ropoxid 501 epoxy resin based on bisphenol A. The synthesized product was crosslinked with ethylenediamine, in the presence of poly(diethylene adipate lactate)diol (PDEAL), as a biodegradable external plasticizer. The composite materials (networks) were analyzed by infrared spectroscopy, differential scanning calorimetry and thermogravimetry. The values of density, volume shrinkage, water absorption and fungicidal action of the synthesized networks were also evaluated. The presence of the silver in the epoxy networks led to important modifications of the resin properties towards the fungicidal action.

---

Opisano syntezę nowych, różniących się składem usieciowanych etylenodiaminą układów opartych na otrzymywanej z bisfenolu A żywicy epoksydowej i soli srebrowej sulfatiazolu z udziałem poli(adypiniano-mleczanu dietylowego) (PDEAL) użytego w charakterze biodegradowalnego plastyfikatora zewnętrznego (tabela 1). Produkty te charakteryzowano metodami IR (rys. 1 i 2), DSC (tabela 4, rys. 3) oraz termograwimetrii (rys. 4). Ponadto określano gęstość, skurcz objętościowy (tabela 2) i absorpcję wody (tabela 3) uzyskanych usieciowanych układów. Wyniki analizy IR prowadzą do wniosku, że srebrowa pochodna sulfatiazolu zostaje wbudowana w sieć żywicy epoksydowej. Ustalono, że obecność PDEAL zmniejsza skurcz objętościowy i gęstość usieciowanych produktów oraz obniża ich temperaturę zeszklenia. Obecność srebra nadaje natomiast produktom aktywność grzybobójczą, pogarszając jednocześnie ich termostabilność.