Adhesion measurement of coating made of mononitrides and composite materials by the scratch method.

Theoretical assumption and experimental results concerning the technological and functional quality of thin, hard coatings produced on cutting edges are described. Mononitrides and composite material coatings were produced on SW7M (S4) high-speed steel by the arc-plasma method. The adhesion force of the CrN, TiN, ZrN, (TiCr)N, (TiZr)N, (TiNbCr)N, (Ti0,85Cr0,15)N, (TiCr0,15Zr)N and (TiCr0,25Zr)N coatings to the substrate was estimated using the scratch test. The usefulness of this non-destructive method, both in a laboratory and industry practice, is stressed. On the base of investigation results it can be stated that hardness of coatings have influence on a critical load.

---

Teoretyczne założenia i wyniki badań eksperymentalnych dotyczące jakości technologicznej i użytkowej cienkich, twardych powłok wytwarzanych na ostrzach skrawających. Powłoki z monoazotków i materiałów złożonych były wytwarzane na stali szybkotnącej SW7M (S4) metodą łukowo-plazmową. Pomiary siły adhezji powłok CrN, TiN, ZrN, (TiCr)N, (TiZr)N, (TiNbCr)N, (Ti0,85Cr0,15)N, (TiCr0,15Zr)N i (TiCr0,25Zr)N do podłoża oceniano za pomocą testu na zarysowanie. Podkreślono przydatność tej nieniszczącej metody zarówno w warunkach laboratoryjnych, jak i w praktyce przemysłowej. Na podstawie wyników badań stwierdzono istotny wpływ twardości powłok na wartość obciążenia krytycznego.