Characteristics of sulphide scale and internal sulphur-rich precipitates in carbon steel by SEM and TEM.

Characteristics of sulphide scale and internal sulphur-rich precipitates in K18 carbon steel after 11 years of service in a refinery furnace environment have been examined in order to beter understand the mechanism of damage to the steel under the influence of sulphur at elevated temperatures. Scanning and transmission electron microscope techniques have been involved in the study. Diffusion paths of the sulphur in the steel have been indicated and two kinds of sulphur-rich precipitates have been presented: degraded cementite particles, additionally enriched in manganese, chromium and silicon, and iron sulphide inclusions that formed after the former particles had completely disappeared.

---

Badano charakterystyczne cechy zgorzeliny siarczkowej i wewnętrznych wydzieleń zawierających siarkę w stali węglowej K18 po 11 latach pracy w piecu rafineryjnym w celu lepszego poznania mechanizmu niszczenia stali pod wpływem siarki w podwyższonych temperaturach. W badaniach wykorzystano technikę elektronowej mikroskopii - skaningowej i transmisyjnej. Wskazano drogi dyfuzji siarki w stali oraz przedstawiono dwa rodzaje wydzieleń zawierających siarkę: zdegradowane cząstki cementytu, dodatkowo wzbogacone w mangan, chrom i krzem oraz wtrącenia siarczków żelaza utworzone po całkowitym zaniku cząstek wymienionych w pierwszej kolejności.