Mechanically alloyed intermetallic matrix composites reinforced with carbides or alumina.

The structural tranformations in FeAl-NbC, FeAl-Al2O3 and NiAl-Al2O3 composite powders obtained by mechanical alloying were studied. The milling process of a mixture of Fe, Al, Nb and graphite powders led to the formation of an amorphous structure. The crystallisation processes resulted in two-phase structure consisting of ordered FeAl intermetallic compound and NbC. Composite powders containing Al2O3 were formed due to the reduction reaction of hematite or nickel oxide by Al, during the ball milling process. All obtained composite powders revealed a nanocrystalline structure of both phases (intermetallic and alumina).

---

W pracy przedstawiono wyniki badań strukturalnych proszków kompozytowych FeAl-NbC, FeAl-Al2O3 i NiAl-Al2O3 otrzymanych metodą syntezy mechanicznej. W przypadku kompozytu FeAl-NbC mieszaninę wyjściową stanowiły proszki Fe, Al, Nb i grafitu. Efektem procesu ich mielenia było utworzenie stopu o strukturze amorficznej. Jego krystalizacja prowadziła do uzyskania dwufazowej struktury FeAl-NbC. Proszki kompozytowe z Al2O3 formowały się w wyniku reakcji redukcji hematytu lub tlenku niklu za pomocą Al, w procesie mielenia odpowiednich mieszanin proszkowych. Uzyskane proszki kompozytowe charakteryzowały się nanokrystaliczną strukturą.