Quantitative description of nickel aluminide structure evolution in Al-(Al2O3)p composite.

Composites materials Al-(Al2O3)p with nickel aluminides formed in situ were obtained as a result of axis pressure sintering in vacuum. The effect of the sintering temperature on the structure was analysed by quantitative metallography methods. An increase of mean particles plane section area with sintering temperature was confirmed. Changes in the shape factor of aluminides formed as a result of interaction between nickel and aluminium matrix were noticed. Differences in the structure of multilayers aluminides were also observed.

---

Materiały kompozytowe Al-(Al2O3)p zawierające aluminidki niklu, powstałe in situ w wyniku oddziaływania proszku niklu z osnową aluminiową, otrzymano metodą osiowego prasowania na gorąco w próżni. Metodami metalografii ilościowej analizowano wpływ temperatury spiekania na strukturę czastek aluminidków niklu. Stwierdzono wzrost średniego pola powierzchni płaskiego przekroju cząstek wraz ze wzrostem temperatury spiekania oraz różnice wartości współczynnika kształtu. Obserwowano także różnice w strukturze aluminidków wykazujących budowę warstwową.