Fracture toughness of welded joints materials in ignalina NPP steam pipelines

The paper presents an investigation of fracture toughness of welded joint metals in Ignalina NPP steam pipelines DU-300 and DU-630. Main metal steels 08X18N10T and 16GS, weld metal welded by manual and automatic arc method using the wire SV-0419N11M3 and electrodes EA-100/10U or EA-100/10T, weld metal welded by manual arc method using the wire SV-08GS2 and electrodes UONI13/55 and heat affected zone metal of welded joint of steel 08X18N10T were investigated. In compact specimens sharp fatigue cracks were initiated and using fracture compliance testing method crack resistance curves, J integral versus crack length (J-R curve), limit values of stable crack extension Damax and critical values of JIc integral were obtained.

---

W pracy opisano badania odporności na pękanie połączeń spawanych w rurociągach parowych wykonanych z Ignaliny NPP. W próbkach kompaktowych wyinicjowano pęknięcia zmęczeniowe i sporządzono dla nich krzywe J - R. Określono także graniczną wartość długości szczeliny Damax oraz krytyczną wartość całki J (JIc).