Influence of microstructure and Laser Shock Processing (LSP) on the corrosion behaviour of AA2050-T8

The corrosion behaviour of AA2050-T8 was studied after polishing and after LSP treatment using microcapillaries and the SVET. After polishing, both pitting at constituent particles and intergranular corrosion were observed. By contrast, no intergranular corrosion / pits developed in the matrix after LSP. In addition, there is an anodic shift of the pitting potential of sites containing particles. Beneficial influence of LSP on corrosion behaviour of AA2050-T8 was also demonstrated using the SVET. The local current was systemically lower after LSP treatment.

---

Korozyjne zachowanie się stopu aluminium AA2050-T8 było badane po mechanicznym polerowaniu i po obróbce laserowej, za pomocą Techniki Skaningowej Elektrody Wibrującej (SVET) i mikro-kapilar. Na próbkach polerowanych zaobserwowano korozję wżerową i międzykrystaliczną w 0,1M NaCl. Z kolei osnowa próbek poddanych obróbce laserowej była odporna na korozję międzykrystaliczną i wżerową. Dla miejsc zawierających wydzielenia obserwowano przesunięcie potencjału przebicia w kierunku anodowym. Korzystny wpływ obróbki laserowej na odporność korozyjną stopu aluminium AA2050-T8 wykazały badania za pomocą SVET. Dla próbek po laserowej obróbce zawsze rejestrowano niższy prąd niż dla próbek polerowanych.