TiC and Al-Ti-C skeletons produced by combustion synthesis

A porous skeleton of TiC carbide was successfully fabricated by combustion synthesis ignited in a microwave field. The synthesizing temperature has been remarkably affected by the time of ball milling or positioning in a single mode microwave reactor. The combustion products were characterized by XRD and SEM investgatons. To moderate the reaction and avoid the explosion mode, an aluminium powder was added to the mixture. The prepared TiC, Al-Ti-C skeletons were next infiltrated with an AlSi12 aluminium alloy by the squeeze casting method. The composite materials exhibited a relatively homogeneous microstructure with low porosity.

---

Porowate szkielety z węglika TiC zostały wytworzone poprze syntezę spaleniową aktywowaną w polu mikrofalowym. Na temperaturę syntezy znacząco wpływa czas mechanicznego mieszania proszków wyjściowych oraz pozycja próbki w polu reaktora mikrofalowego. Produkty reakcji zostały zbadane w oparciu o analizę XRD oraz na mikroskopie skaningowym z sondą BSE. W celu wyhamowania dynamiki reakcji i uniknięcia eksplozyjnego przebiegu do mieszaniny wyjściowej dodawano proszek Al. Wytworzone kształtki TiC, Al-Ti-C nasycano stopem aluminium AlSi12 metodą prasowania w stanie ciekłym. Kompozyty charakteryzowały się dostatecznie jednorodną mikrostrukturą z nielicznymi porowatościami.