Phase changes in super fine-grained steel during continuous cooling process

In this work the investigations of the steel with 0,1 %C, 0,8 %Mn and Al addition which favor the fine structure of steel obtaining were presented. During investigations the specimens were heated to temperature: 910 °C and 1100°C and austenitized in these temperatures by 300 s, and then cooled with cooling rate: 0.1÷150 °C/s. The specimens after the cooling process were investigated in metallographic way to reveal details of formed structure and the Vickers’ hardness were measured. As a result of complex investigation two CTPc diagrams were elaborated.

---

W pracy przedstawiono badania stali o zawartości około 0,1 %C, 0,8 %Mn z dodatkiem Al, który sprzyja powstawaniu w stali drobnoziarnistej struktury. Podczas badań próbki nagrzewano do temperatur: 910 i 1100 °C, austenityzowano w tych temperaturach przez 300s, a następnie chłodzono z szybkościami z zakresu: 0,1÷150 °C/s. Próbki po chłodzeniu poddano badaniom metalograficznym w celu ujawnienia powstałej struktury oraz określono twardość metodą Vickers’a. W wyniku przeprowadzonych kompleksowych badań opracowano dwa wykresy CTPc dla badanej stali.