Isothermal phase transformation occuring in the experimental designed superfine-grained constructional steel

Increasing the mechanical properties of constructional steel by applicable thermoplastic treatment advisable due to the relatively low price. In this work the investigations of steel with 0.1 %C, 0.8 %Mn and Al addition which favour the fine-grained structure of steel arising were done. As a result of complex investigations the TTT diagram was elaborated. The dilatometer tests were done. Test results allow to construct true diagrams of phase transformation occuring during isothermal heating process. The specimens were heated to austenitizing temperature, austenitized and then cooled with cooling rate 150 °C/s up to the isothermal heating temperature. After that the specimens were investigated in metallographic way to reveal detalis of formed structure and the Vickers’ hardness were measured.

---

Podniesienie właściwości wytrzymałościowych stali konstrukcyjnych poprzez odpowiedni rodzaj obróbki cieplnoplastycznej jest bardzo pożądane ze względu na relatywnie niską cenę. W pracy przedstawiono badania stali o zawartości około 0,1 %C i 0,8 %Mn z dodatkiem Al, dzięki któremu powstaje w stali drobnoziarnista struktura. W wyniku przeprowadzonych badań opracowano wykres CTPi. Zakres eksperymentu obejmował przeprowadzenie badań dylatometrycznych, których wyniki umożliwiły budowę rzeczywistych wykresów przemian fazowych zachodzących podczas wygrzewania izotermicznego. Próbki nagrzewano do temperatury austenityzowania, austenityzowano, a następnie chłodzono z szybkością krytyczną do temperatury wygrzewania izotermicznego. Próbki po chłodzeniu poddano badaniom metalograficznym w celu określenia struktury, która powstała podczas eksperymentu oraz określono twardość sposobem Vickersa.