Modification of Eutectic Mgl7All2 Phase with Yttrium in Mg-Al-Zn Alloys

The modification of Mg17Al12 eutectic phase in Mg-Al-Zn alloys with yttrium (Y) was investigated in the work. As-cast microstructure analysis of unmodified Mg-Al-Zn alloys indicated that the Mg17Al12 eutectic phase was continuous and reticulated. It turned out that yttrium admixture to Mg-Al-Zn casting alloys has important influence on the crystallization of Mg17Al12 phase. When the Y content is 0.3 wt %, the effect of Y can be ignored and no Y-containing compound is formed. When the Y content is 0.6 and 0.9 wt. %, a new phase (Al2Y) occurs in the alloy while the preferred growth manner of the Mg17Al12 eutectic is effectively suppressed. Simultaneously the MgI7Al12 eutectic breaks the primary network structure and distinctly exhibits a modified fine grained morphology. When the Y content is further increased to 1.2 wt. %, the Al2Y phase becomes coarser and Mg17Al12 transforms into a flock-shape structure.

---

W pracy zbadano wpływ modyfikacji fazy eutektycznej Mg17Al12 w stopach Mg-Al-Zn za pomocą itru (Y). Analiza mikrostrukturalna odlewów niezmodyfikowanych stopów Mg-Al-Zn wykazała ciągłą siatkową strukturę fazy eutektycznej Mg17Al12. Wykazano, że wprowadzenie itru do stopu Mg-Al-Zn ma znaczący wpływ na krystalizację fazy Mg17Al12. Gdy zawartość itru wynosi 0,3 % mas., jego wpływ jest mało znaczący i nie tworzy się żaden związek zawierający itr. Przy zawartości itru wynoszącej 0,6 % i 0,9 % mas. występuje nowa faza (A12Y) i uprzywilejowany wzrost kryształów fazy Mg17Al12 jest skutecznie zahamowany. Wówczas eutektyczna faza Mg17A112 wykazuje wyraźnie zmodyfikowaną morfologię. Gdy zawartość itru dalej wzrasta do 1,2% mas., faza A12Y staje się bardziej gruboziarnista, a faza Mg17Al12 zmienia formę strukturalną na kłaczkowatą.