Influence of gas nitriding conditions on formation of nitrided layer on duplex stainless steel

The paper presents results of the investigations on the influence of gas nitriding parameters on layer formation on ferritic-austenitic stainless steel (X2 CrNiMoN 22 5 3.)- The ion sputtering was applied as an activation technique before the gas nitriding. Hydrogen was used as sputtering gas at 3-5 Pa. The nitriding was conducted in ammonia atmosphere in temperature 673-823 K. The morphology and phase composition of the layers were evaluated using light microscopy and X-ray diffraction methods. Moreover, kinetics of the process was evaluated. The thickness measurements were based on statistic plan of experiment.

---

W artykule przestawione zostały wyniki badań nad wpływem parametrów procesu azotowania gazowego na tworzenie warstw na stali ferrytyczno-austenitycznej (X2 CrNiMoN 22 5 3). Jako obróbkę aktywującą zastosowana proces rozpylania jonowego, który bezpośrednio poprzedzał azotowanie. Obróbkę aktywacyjną prowadzono w wodorowej plazmie niskotemperaturowej przy ciśnieniu 3-5 Pa. Obróbkę gazową prowadzono w atmosferze amoniaku w mieszaninie z produktami jego dysocjacji w temperaturze 673-823 K. Zbadano morfologie oraz budowę fazową warstw azotowanych. Dodatkowo wyniki badań zostały poparte obliczeniami statycznymi, które pozwoliły dokonać oceny wpływu parametrów obróbki cieplno-chemicznej na kinetykę wzrostu warstwy azotowanej na stali duplex.