Quantitative analysis of microstructure in AE44 magnesium alloy after long-term annealing

The microstructure and microstructural stability of die-cast AE44 (Mg-4A1-4RE) alloy were investigated by quantitative metallography, X-ray diffraction, scaning electron microscopy and transmission electron microscopy. It is shown that formation of A12RE after long-term annealing at 250°C is not related to the decomposition of AlnRE3, as reported in the literature, but, rather, it is associated with the supersaturation of rare earth atoms in the matrix and probably related to the decomposition of AI2.12RE0.88 phase. The high thermal stability of AlnRE3 compound located at the interdendritic regions impedes the grain growth in AE44 alloy at 250°C.

---

W artykule przedstawiono wyniki badań struktury i stabilności strukturalnej odlewanego ciśnieniowo stopu magnezu AE44 (Mg-4A1-4RE). Badania przeprowadzono z wykorzystaniem metalografii ilościowej, rentgenowskiej analizy strukturalnej, elektronowej mikroskopii skaningowej i transmisyjnej. Stwierdzono, że powstawanie fazy A12RE podczas długotrwałego wygrzewania w 250°C nie jest związane z przedstawionym w literaturze rozpadem fazy AlnRE3. Proces ten może być związany z przesyceniem roztworu stałego pierwiastkami ziem rzadkich i rozpadem fazy Al2.12RE0.ffl. Wysoka stabilność termiczna fazy AlnRE3, znajdującej się w przestrzeniach międzydendrytycznyeh, zapobiega rozrostowi ziarna w 250°C.