Structure and properties of WC1-x/C coatings deposited by reactive magnetron sputtering on ASP2023 HSS steel and monocrystalline Si substrates

New type WC1-x/C coatings have been deposited onto hardened ASP2023 HSS and Si substrates by means of a reactive magnetron sputtering. After deposition the structure and properties of the coatings have been analysed with use of SEM, EDS, XRD, Raman spectrometry, nanoindentation, nanoscratching, ball-on-disk dry sliding wear of the coatings against ceramic ZrO2 ball as well as of macroscratch test. Very useful properties of coatings (good adhesion, low friction and high resistance to wear during dry sliding) can be recommended for numerous applications in the machine-building, automotive, power, aircraft and aerospace industries and in many other branches of modern industry.

---

Nowego rodzaju powłoki WC1-x/C osadzono na podłożach ze stali szybkotnącej ASP2023 oraz krzemowych metodą reaktywnego rozpylania magnetronowego. Po osadzeniu strukturę i właściwości powłok zbadano za pomoca takich technik, jak: SEM, EDS, XRD, spektrometria Ramana, nanoindentacja, nanoscratch, tarcie suche metodą kulka-krążek względem kulki ZrO2, jak również metodą macro-scratch. Bardzo korzystne cechy osadzonych powłok (dobra adhezja, niski współczynnik tarcia suchego i jednocześnie wysoka odporność na zużycie cierne) mogą znaleźć zastosowanie w przemyśle maszynowym, samochodowym, energetyce, lotnictwie, przemyśle kosmicznym i innych gałęziach przemysłu.