Influence of continuously cast bloom’s heating strategy on cracks occurence in low-alloyed Cr-Mo based steel 25CrMo4

In the case of the Cr-Mo based low-alloyed steel hot rolling of square billets from round continuously cast blooms is complicated by fact that internal cracks are detected during ultrasonic inspection at the end of production process on cooling bed. Final quality of hot rolled billets is influenced especially by casting speed and overheating temperature in a tundish, heating conditions in soaking pit and hot rolling factors. In our paper it is demonstrated that for optimization of heating process before hot rolling it is necessary to respect thermophysical properties of low-alloyed Cr-Mo based steels. Improved heating plan led to statistically significantly lower occurence of central cracks in hot rolled billets with minimum financial cost increase.

---

Walcowanie bloków o przekroju kwadratowym stali Cr-Mo z ciągle odlewanych kęsów okrągłych jest komplikowane przez fakt, iż pęknięcia wewnętrzne są ujawniane dopiero podczas kontroli ultradźwiękowej na końcu całego procesu technologicznego. Na jakość wyjściową wyrobu walcowanego mają wpływ zwłaszcza prędkość odlewania, temperatura przegrzania stali w kadzi pośredniej, strategia grzania w piecu wgłębnym oraz warunki walcowania. Artykuł zwraca uwagę na fakt, iż strategia grzania przed walcowaniem musi uwzględniać właściwości termofizyczne stali niskostopowych Cr-Mo. Usprawniona strategia grzania prowadziła do znacznego zmniejszenia liczby pęknięć w wyrobach walcowanych przy minimalnym podwyższeniu kosztów.