Kinetics of phase transformations of undercooled austenite in tool steels of a different chromium content

The kinetics of phase transformations of undercooled austenite in two tool steels of a different chromium content is presented in the form of CCT diagrams. Investigations were performed for two tool steels containing 2.06% and 2.98% of chromium. A carbon content was app. 0.8% and the remaining alloying elements were the same in both steels. The optimal austenitizing temperature was determined on the bases of dilatometric and metallographic investigations and hardening tests. It was found, that the chromium content leads to the increase of time to the start of the pearlitic transformation while it does not influence the beginning of the bainitic transformation and M S temperature.

---

Kinetykę przemian fazowych przechłodzonego austenitu dwóch stali narzędziowych o rożnej zawartości chromu przedstawiono w formie wykresów CTPc. Badania wykonano na dwóch stalach narzędziowych o zawartości chromu 2,06% i 2,98%. Przy zbliżonej zawartości węgla (ok. 0,8%) i pozostałych pierwiastków stopowych. Optymalną temperaturę austenityzowania określono na podstawie badań dylatometrycznych, metalograficznych i pomiarów twardości. Stwierdzono, iż w badanych stalach zwiększenie zawartości chromu wpływa na wydłużenie czasu do rozpoczęcia przemiany perlitycznej, natomiast pozostaje bez wyraźnego wpływu na początek przemiany bainitycznej i temperaturę M S.