The evolution of the gradient microstructure of the hard magnetic alloy FeCr30Co8 subjected to plastic deformation by tension combined with torsion

The article presents the results of the microstructure evolution studies of the hard magnetic alloy FeCr30Co8 subjected to deformation by tension combined with torsion. The observations in the longitudinal section of the samples show a formation of a gradient microstructure with the maximum grain refinement in the surface layer of the material. A precipitation of the intermetallic "-phase was also observed, with its largest amount in the zones of the highest deformation. The refinement of the microstructure and the precipitation of the "-phase resulted in a significant increase of hardness at the surface of the material.

---

Praca przedstawia wyniki badań zmian mikrostruktury magnetycznie twardego stopu FeCr30Co8 poddanego odkształceniu przez rozciąganie i skręcanie. Obserwacja przekroju wzdłużnego próbek pokazała tworzenie się mikrostruktury o charakterze gradientowym z maksymalnym rozdrobnieniem ziarna w warstwie wierzchniej materiału. Obserwowano również wydzielenia fazy międzymetalicznej ", której największa ilość wydzieliła się w miejscach intensywnego odkształcenia. Rozdrobnienie mikrostruktury oraz wydzielenie fazy " spowodowało znaczny wzrost twardości materiału na jego powierzchni.