The role of ECAP in densification behaviour of PM aluminium alloy

The present paper focused on the role of ECAP process on the densification behaviour of PM aluminium alloys. An aluminium powder Al-Mg- Si-Cu-Fe was used as material to be investigated. After applying different compacting pressures in the range of 400 to 700 MPa, specimens were dewaxed at 400°C for 60 min. Sintering was carried out in a vacuum furnace at 610°C for 30 min. The specimens were ECAPed for 1 pass. Structural characterization was carried out on the minimum of 10 different image fields for pressed and sintered specimens as well ECAPed specimens. A decrease of porosity was revealed for all specimens.

---

Praca dotyczy zastosowania technologii przeciskania przez kanał kątowy ECAP dla zagęszczania proszków stopów aluminium. Badano proszek stopu aluminium Al-Mg-Si-Cu-Fe. Po zastosowaniu prasowania przy różnych ciśnieniach od 400÷700 MPa, próbki oczyszczano z substancji organicznych przez wyżarzanie w 400°C przez 60 min. Następnie próbki spiekano w temperaturze 610°C przez 30 min. Następnie poddano je przeciskaniu w kanale ECAP. Porównano struktury próbek spiekanych i przeciskanych w kilku miejscach i stwierdzono znaczny spadek porowatości.