Domain structure of sintered Alnico 8 magnets

Sintered magnets were produced from mixture of powders, having Alnico 8 alloy composition. Their microstructure as well as domain structure were examined. The modulated structure produced by the thermomagnetic treatment has a form of a chessboard, composed of particles of about 30 nm in side. It has been observed that the domain structure has the form of interaction domains, and is composed of the bands of single domains which on their normal plane have the width of 150÷180 nm and the length from 400 nm to 1 ?m, while on the plane parallel to magnetic field these dimensions are much more differentiated and assume the values of 100÷300 nm and from 500 nm to 1 ?m for the width and length, respectively. Interaction domains are macroscopic areas composed of ordered monodomain particles magnetised in one direction.

---

Wytworzono magnesy spiekane ze stopu Alnico 8 oraz zbadano ich mikrostrukturę i strukturę domenową. Otrzymana w wyniku obróbki cieplno-magnetycznej modulowana struktura ma postać szachownicy, utworzonej przez cząstki o boku ok. 30 nm. Stwierdzono, że struktura domenowa ma formę domen wzajemnego oddziaływania i jest złożona z pasm pojedynczych domen, które na powierzchni prostopadłej mają szerokość 150÷180 nm i długość od 400 nm do 1 ?m, a na płaszczyźnie równoległej do pola wymiary te są bardziej zróżnicowane i wynoszą odpowiednio 100÷300 nm i 500 nm do 1 ?m. Domeny wzajemnego oddziaływania stanowią makroskopowe obszary składające się z monodomenowych, uporządkowanych cząstek namagnesowanych w jednym kierunku.