Problems during rolling of FeNi type alloys

The paper deals with problems of manufacturing of flat products for electrical engineering components from iron-nickel based alloys. Elimination of surface defects and minimization of side edge cracking during forming is the goal solved in the Eureka project. Grain boundary segregations and recrystallization in FeNi alloys (47-^50 % Ni) are factors causing bad yielding ability during rolling operations. Therefore main attention is dedicated to casting conditions (segregations and primary structure appearance) and rolling (dynamic recrystallization) in particular. Cast and wrought microstructural states are studied both in failed and in faultless sheets. Cracks and grain boundaries are studied by electron microscopy, fractography and chemical microanalysis.

---

Praca koncentruje się na wytwarzaniu płaskich wyrobów przeznaczonych do zastosowań na elementy w elektrotechnice, wykonanych ze stopów żelazo-nikiel. Eliminacja defektów powierzchniowych i pękania podczas kształtowania była celem do rozwiązania w projekcie Eureka. Segregacja granic ziarn i rekrystalizacja w stopie FeNi (47+50 % Ni) są przyczyną uzyskiwania niewłaściwej granicy plastyczności podczas operacji walcowania. Dlatego w szczególności główną uwagę kieruje się na warunki odlewania (segregacja i struktura pierwotna) i walcowania (dynamiczna rekrystalizacja). Mikrostruktura po odlewaniu i w stanie po przeróbce plastycznej była badana na uszkodzonych i bezusterkowych arkuszach. Strukturę i proces pękania badano na mikroskopie elektronowym, metodami fraktografii i mikroanalizy chemicznej.