Asymmetry of magnetic properties of conventional grain-oriented electrical steel with relation to 2D measurements

Samples of 3% Si-Fe 0.27 mm thick conventional GO in a form of single strips 30 x 305 mm, cut at every 10 degrees from 0 degrees (synonymous with rolling direction) to 170 degrees were measured under sinusoidal flux density up to 1.5 T at 50 Hz and 400 Hz. The measured results show that the anisotropy of power loss and permeability is symmetrical about the rolling direction. The irregularities in the curves are caused mainly by the quality of the laser cutting and differences in the local properties of the steel sheet.

---

Artykuł opisuje pomiary wykonane na próbkach elektrotechniczej blachy zorientowanej 3% Si-Fe pociętych w paski o wymairach 30 x 305 x 0.27 mm pod kątami od 0 do 170 stopni (z krokiem co 10 stopni). Próbki zmierzono w warunkach sinusoidalnej indukcji do wartości 1,5 T i przy częstotliwosciach 50 i 400 Hz. Zmierzone wyniki wykazują, że anizotropia strat mocy i przenikalności jest symetryczna względem kierunku walcowania. Ewentualne nieregularności w zmierzonych krzywych wynikają z jakości obróbki laserowej i lokalnych własności arkusza blachy.