Carbon fiber - based composite with silicon - containing polymer matrix

Composite based on polysiloxane resins and carbon fibers as reinforcing elements have been investigated. Polysiloxane- based resins were used as a matrix precursor. Wet - winding technique was employed to prepare the unidirectional laminates. The parameters of this stage in the processing of composite were optimised. Unidirectional composite samples with organic matrix were subject to thermal treatment up to 1500°C. Mechanical properties of the samples after various stages of manufacturing were determined. Thermal resistance of the composite after heat treatment to 900 and 1500°C of organic matrix reinforced with carbon fibers was studied.

---

Przedmiotem badań były kompozyty wytworzone z włókien węglowych jako elementów zbrojących osnowę polisiloksanową. Zastosowano technikę ciekłej impregnacji włókien żywicą celem wytworzenia laminatów jednokierunkowych. W pracy określono warunki formowania laminatów, z których następnie wytworzono jednokierunkowe próbki kompozytowe. Próbki takie poddawano obróbce termicznej do temperatury 1500°C. Określono właściwości mechaniczne próbek kompozytowych w różnych fazach ich przetwarzania. Badano również odporność termiczną otrzymanych próbek kompozytowych po obróbce termicznej w temperaturach 900 i 1500°C.