Chemical/electrochemical methods for the preparation of graphite multiintercalation compounds

In this work, the process of the subsequent intercalation of HSO4H2SO4 into CrO3-GIC examined. CrO3GICICs are prepared with two different chemical methods: this is, intercalation from the CrO3/CH3COOH solution according to the Platzcr and de la Martiniere procedure and intercalation of CrO3 from Cr03/HCl solution. Furthermore, the preparation of graphite multiintercalation compound consisted with two different intercalates CrO3 and ZnCl2 from the mixture of graph ite/CrO32 HC1 was performed. The intercalation process of both intercalates CrO3 and ZnCl2 into graphite has been confirmed by cyclic voltammetric technique. Upon the successive intercalation of HSO4/H2S04 the anodic and cathodic effects characteristic for the presence of ZnCl2 and CrO3 have been served in the voltammogram. This suggests the formation of quaternary CrO3/ZnCI2-H2SO4-GIC.

---

Przedstawiono proces biinterkalacji Hsub>2S04 zachodzący w CrO3IZG. Interkalacja CrO3 w grafit była prowadzona z dwóch mieszanin: grafit/Cr03/HCl oraz grafit/CrO3CH3COOH. Ponadto przeprowadzono próbę jednoczesnej interkalacji dwóch interkalatów CrO3 oraz ZnCl2 celem otrzymania układu multiinterkalacyjnego. Aby stwierdzić czy zaszedł proces interkalacji CrO3 oraz ZnCl2 w grafit, produkt reakcji był badany metodą cyklicznej woltamperometrii w 95 % H2SO4. Na podstawie otrzymanych krzywych woltamperometrycznych stwierdzono obecność obu interkalatów (CrO3 oraz ZnCL2 w matrycy grafitowej. Ponadto, w wyniku anodowego utleniania CrOI3ZnCI2-IZG w 95% H2SO4 otrzymano układ poczwórny CrO3/ZnCl2H2SO4- grafit.