The use of molybdenate metod to estimate the molecular composition of sodium water glasses solutions

By means of method of ß-molybdenosilicic acid synthesis (co-called molybdenate method), the molecular composition of Polish-made concentrated technical sodium silicates of different moduli, was studied. The concentration of SiO2 occurring in active form, i.e. forming ß-molybdenosilicic acid, and inactive form – not reacting with molybdenic acid, was estimated. It was found that the kinetics of ß-molybdenosilicic acid synthesis depends on the silicate modulus, i.e. the Na:Si molar ratio. With the decrease of Na:Si molar ratio, the reaction rate constants also decrease. The rate of heteropolyacid formation depends on the type of silicate forms existing in the solution. The higher level of silicate condensation, the reaction is slower. It’s related to the higher amount of polymeric anions.

---

Metodą syntezy kwasu ß-molibdenokrzemowego, tzw. metoda molibdenianowa, badano skład molekularny stężonych różnomodułowych krzemianów sodowych technicznych wyprodukowanych w Polsce. Określono zawartość SiO2 występującej w formie aktywnej tzn. tworzącej kwas ß-molibdenokrzemowy oraz nieaktywnej – nie reagującej z kwasem molibdenowym. Stwierdzono, że kinetyka syntezy kwasu ß-molibdenokrzemowego zależy od modułu krzemianowego tj. stosunku molowego Na:Si. Z obniżeniem się stosunku Na:Si wartości stałych szybkości reakcji maleją. Szybkość powstawania heteropolikwasu zależy od rodzaju form krzemianowych w roztworze; im wyższy stopień kondensacji krzemianu tym reakcja jest wolniejsza. Jest to związane z obecnością coraz większej ilości polimerycznych anionów.