Voltammetric determination of caffeine at pt/carbon nanotubes composite modified glassy carbon electrode

Platinum nanoparticles (Pt) supported on carbon nanotubes (CNTs) were used to modify glassy carbon electrode (GCE) in order to determine caffeine. In 0.01 mol L-1 H2SO4 solution, the modified electrode (Pt-CNTs-GCE) showed obvious electrocatalytic activitytowards oxidation of caffeine. The oxidation peak current increased significantly and the oxidation potential shifted negatively. All experimental parameters were optimised.The magnitude of the oxidation peak current of caffeine was proportional to its concentration over the range 1.0 x 10-6-1.0 x l0-4mol L-1 and detection limit was 2 * 10-7 mol L-1. Relative standard deviation (RSD) of seven replicate determinations of l x 10-5 mol L-1caffeine was 2.03%. The proposed method was applied to the determination of caffeine in real samples with the recovery in the range from 96.5% to 102%.

---

Nanocząsteczki platyny wsparte węglowymi nanorurkami użyto do modyfikacji elektrody z węgla szklistego w celu oznaczenia kofeiny. Zmodyfikowana elektroda wykazywała elektrokatalityczną aktywność w procesie utlenienia kofeiny. Prąd utleniania kofeiny wzrastał a potencjał piku woltamperometrycznego stawał się bardziej ujemny. Zoptymalizowano parametry eksperymentalne. Wysokość piku woltamperometrycznego rosła liniowo ze stężeniem kofeiny w zakresie 1.0x10-6-1.0x l O-4 mol L-1. Granica wykrywalności wyniosła 2 x 10-7mol L-1 a względne odchylenie standardowe dla stężenia l x 10-1mol L-1 wyniosło2.03%. Opracowaną metodę zastosowano do oznaczania kofeiny w rzeczywistych próbkach. Odzysk metody wyniósł od 96.5 do 102%.