Wear behaviour and tribochemical reactions of low molecular alcohols under boundary lubrication of the steel-on-aluminium system.

Tribochemistry of Alcohols is very complex and important from the practical piont of view. This paper relates to the research aiming at better understanding of the aliphatic alcohol tribochemistry.Using mostly the steel ball-on-alluminium disc friction system experiments were carried out to generate tribochemical reaction s on the aluminium discto analyse the formed deposits FTIR surface analysis was used.New adsorptionbandsmostly in the region of 1530-1550 cm-1 were found They are asssigned to the specific structure of organometallic compounds with -in many cases-include duble bonding in the reion of 1600-1650 cm-1.It was also found that the dissocitation constant (pKa)values of C1-C$alcohols control the steel ball wear for both steel-on-aluminium and steel-on-steelsystems.

---

W niniejszym artykule przedstawiono wyniki badań, mających na celu zrozumienie tribochemii alkoholi alifatycznych. Eksperymenty, polegające na generowaniu reakcji tribochemicznych na powierzchni dysku aluminiowego, przeprowadzano głównie w układzie tarciowym stal-aluminium. Do analizy odłożonych depozytów zastosowano mikrospektrofotometrię FTIR. Stwierdzono obecność nowych pasm absorpcyjnych zwłaszcza w obszarze 1530-1550 cm-1.Są one przypisywane specyficznej strukturze związków organometalicznych które w wielu przypadkach posiadaja wiązanie podwójne 91600-1650cm-1) Stwierdzono również że wartośc stałej dysocjacji pKa) dla alkoholi C1-C4 wpływa na wielkość zużycia kulki stalowej zarówno w układzie tarciowym stal-aluminium jak również w układzie sta-stal.