Internal friction in pure Co and CoPt alloy during ordering

Internal friction, the shear modulus defect and magnetic susceptibility behaviour of disordered equi-atomic CoPt alloy and pure cobalt has been investigated during annealing with heating rates 6 K/min and 2 K/min up to 850 K using an inverted torsional pendulum. The internal friction peak at 720 K in cobalt near the martensitic phase transition and in CoPt at 700 K, whose amplitude increase with decreasing heating rate, suggest a superposition of two effects: a rapid, thermally-activated, reorientational relaxation leading to short-range order, and a slower, migrational, structural relaxation leading to long-range order.

---

Zbadano tarcie wewnętrzne, wskaźnik modułu sprężystości postaciowej i podatność magnetyczną stopu CoPt (50% at. Pt) w stanie nieuporządkowanym, uzyskanym w wyniku oziębienia, podczas wyżarzania do 850 K przy wzrostach temperatury 6 K/min, i 2 K/min stosując odwróconą skręcarkę wahadłową. Zaobserwowano maksimum tarcia wewnętrznego w CoPt przy 700 K oraz w monokrysztale kobaltu w 720 K w pobliżu martenzytycznej przemiany fazowej, wzrastające w miarę obniżania szybkości wzrostu temperatury wyżarzania. Otrzymane rezultaty sugerują superpozycję dwóch efektów relaksacyjnych: szybkiego, termicznie aktywowanego efektu reorientacyjnego, prowadzącego do uporządkowania bliskiego zasięgu, oraz wolniejszego, migracyjnego efektu relaksacji strukturalnej, powodującego uporządkowanie dalekie.