The evaluation by means of microindentation and sclerometry of changes in properties after electron beam irradiation of polyethylene GUR 1050

With the aim to increase the resistance of GUR 1050 polyethylene to plastic deformation and abrasive wear, modification through radiation was applied. Compression tests of up to 300 MPa showed an increase in resistance to permanent deformation. This has been confirmed with microindentation and sclerometry tests. Scratch test indicated a lower tendency of the carved material to chipping than to uplift in all operational deformations. The domination of the micromechanism of the formation of ridges allows the material to retain a small decrease in resistance to wear. The parameters of microtests may be used for the purpose of the evaluation and selection of the polymers used in friction joints in medicine and technology.

---

W celu podwyższenia odporności polietylenu GUR 1050 na odkształcenie plastyczne i zużycie ścierne zastosowano modyfikację radiacyjną. Badania w zakresie naprężeń do 300 MPa wykazały wzrost odporności na deformację trwałą. Potwierdzono to testami mikroindentacyjnymi i sklerometrycznymi. Scratch test wykazał, że w całym zakresie odkształceń eksploatacyjnych występuje mniejsza skłonność do wykruszania materiału wyżłobionego niż do jego plastycznego wypiętrzania. Dominacja mikromechanizmu bruzdowania pozwala zachować niewielki spadek odporności na zużycie. Parametry mikrotestów mogą być wykorzystywane do diagnozowania i selekcji polimerów stosowanych w medycznych oraz technicznych węzłach tarcia.