Solidification course of the Al-rich Al-Si-Fe-Mn alloys

In this paper the results of the analysis of the solidification course of the Al-rich alloys containing silicon and transition metals Fe and Mn are presented. Both liquidus and solidus temperature were estimated by means of the differential scanning calorimeter. Simultaneously the microstructure formation stages corresponding with registered thermal effects were revealed by means of the microscopic observations. It was stated that the morphology of the intermetallic phases formed in the precipitation sequence was estimated to be influenced mainly by Fe/Mn ratio whilst the precipitation sequence and temperature of the phase constituents formation were determined by an absolute content of the transition metals. An increase in the silicon content in the examined alloy resulted in some shift of the star of the process of the primary pre-dendrite precipitation into lower transition metals contents.

---

W pracy przedstawiono wyniki analizy przebiegu krzepnięcia stopów aluminium, zawierających krzem oraz metale przejściowe Fe i Mn. Zakres krzepnięcia, temperatura likwidus i solidus zostały wyznaczone za pomocą skaningowego mikrokalorymetru. Równocześnie, posługując się obserwacjami mikroskopowymi , analizowano proces powstawania składników fazowych mikrostruktury stopu. Stwierdzono, że morfologia powstałych faz międzymetalicznych była zdeterminowana wartością wskaźnika Fe/Mn, natomiast o sekwencji i temperaturze wydzielania określonych składników fazowych mikrostruktury decydowała zawartość żelaza i manganu w stopie. Ze wzrostem zawartości krzemu w badanych stopach wiązała się niższa zawartość metali przejściowych konieczna do zainicjowania procesu pierwotnego, pre-dendrytycznego wydzielania poczwórnej fazy międzymetalicznej AlFeMnSi.