Thermal and microstructural characteristics of Cu68.5Ni12P19.5 melt spun ribbon

The Cu68.5Ni12P19.5 alloy was prepared using 99.95 wt % Cu, Cu-P and Ni-P master alloys. The precursors were encapsulated in quartz tubes under vacuum (10^-2 bar) and melted in resistance furnace. Metallographic observations of the alloy were combined with measurement of volume fraction of microstructural constituents in as-cast state. The ribbon was cast using melt spinnig technique. The ribbons were then investigated by means of differential scanning calorimetry (DSC) and differential thermal analysis (DTA). High temperature X-ray studies of the material were made in order to characterize the thermal stability. The characteristics of the alloy are discussed and compared with other experimental data.

---

Stop Cu68.5Ni12P19.5 przygotowano wykorzystując 99,95% wag. Cu, zaprawy Cu-P oraz Ni-P. Składniki te zatapiano w kapsułach kwarcowych w próżni (10^-2 bar) i przetapiano w piecu oporowym. Przeprowadzono badania metalograficzne stopu w stanie lanym oraz wykonano pomiary ułamka objętościowego poszczególnych składników mikrostruktury. Odlano taśmę stosując technikę "melt spinning". Następnie, odlaną taśmę badano wykorzystując różnicową kalorymetrię skaningową (DSC) oraz różnicową analizę termiczną (DTA). W celu określenia stabilności termicznej przeprowadzono wysokotemperaturowe badania w dyfraktometrze rentgenowskim. Otrzymane wyniki porównano i przedyskutowano korzystając z innych istniejących danych eksperymentalnych.