Influence of ausaging on microstructure and mechanical properties of high nitrogen 12% Cr steel for power plant applications

The paper presents an investigation of a martensitic high-nitrogen steel with a 12% Cr content designed for potential applications in power plants. The steel was subjected to ausaging before martensitic transformation or ausaging followed by tempering. The ausaging influenced greatly the precipitation reactions as well as yield strength at elevated temperatures. It was dissolution and reprecipitation of MN- type vanadium nitrides with a face-centered cubic crystal structure which controlled the dispersion of precipitates and thus mechanical properties of the steel.

---

W pracy podjęto badania wysokoazotowej stali o zawartości 12%Cr przeznaczonej do zastosowań w energetyce. Przemiana martenzytyczna w tej stali była poprzedzona starzeniem w zakresie austenitu. Utworzony martenzyt został poddany odpuszczaniu. Schemat stosowanej obróbki cieplnej przedstawiono na rys. 1 oraz w tabeli 1. W pracy wykazano, że mikrostruktura i właściwości mechaniczne są zdeterminowane rozpuszczaniem sie pierwotnych azotków VN i ponownym wydzielaniem się nowych azotków i węglikoazotków w formie dyspersoidu (rys. 3a i 9b). Wielkość i dyspersja nowych wydzieleń silnie zależy od procesu starzenia poprzedzającego przemianę martenzytyczna, które poprawia istotnie właściwości mechaniczne badanej stali.