Crystal lattice rotation in channel-die deformed al bicrystals with {100}<001>/{100}<011> AND {100}<001>/{110}<001> orientations

The issues of band-like inhomogeneties of deformed structure and the evolution of their microtexture components are addressed. The analysis is based on bands development by plane strain compression in {100}<001>/{100}<011> and {100}<001>/{110}<001> oriented high purity aluminium bicrystals with boundary planes situated nearly perpendicular to the compression plane. Substantial progress in understanding the character of these bands was possible due to systematic local orientation measurements using scanning electron microscopy (SEM) equipped with field emission gun (FEG). Goss {110}<001> oriented grains are stable within the range of applied deformations whereas the 'cube' {100}<001> and 'shear' {100}<011> grain orientations are very unstable under plane strain conditions and develop band-like inhomogeneities of deformation.

---

W pracy analizowano formowanie się niejednorodności odkształcenia oraz ewolucję ich wewnętrznej mikrotekstury. Badania prowadzono na bikryształach aluminium o układzie orientacji {100}<001>/{100}<011> i {100}<001>/{110} <001> z granicą ziaren usytuowaną równolegle do płaszczyzny ściskania. Opisu dominujących systemów poślizgu odpowiedzialnych za obserwowane tendencje rotacji sieci krystalicznej dokonano w oparciu systematyczne pomiary orientacji w mikroskopie skaningowym wyposażonym w działo o emisji polowej. Ziarna o orientacji 'goss'{110}<001>są stabilne w szerokim zakresie odkształceń podczas gdy krystality o orientacjach 'cube'{100}<001> oraz 'shear' {100}<011>są silnie niestabilne w próbie nieswobodnego ściskania i sprzyjają rozwojowi pasmowych niejednorodności odkształcenia.