Characterization of the solid residue of enargite Cu3AsS4 after alkaline leaching.

The characterization of solid after alkaline leaching of enargite Cu3AsS4 is discussed. X-ray diffractometry for characterization of the physico-chemical transformations in bulk of source enargite concentrate resulted from alkaline leaching was used. The surface layers of the samples of enargite concentrate were investigated with XPS spectroscopy. The leaching of mechanically activated enargite concentrate with Na2S leads to total extraction of arsenic (the content of As in a solid after leaching is 0.06%) and then decomposition of enargite (Cu3AsS4) with formation of new phases of copper sulphide and jarosite. XPS spectroscopy measurements did not registered the occurrence of arsenic in any chemical form in the sample of solid taken from leaching system.

---

Przedyskutowano charakterystyczne cechy suchej pozostałości po alkalicznym ługowaniu enagritu Cu3AsS4. W celu charakteryzacji fizykochemicznych przemian w suchej pozostałości posłużono się dyfraktogramem rentgenowskim koncentratu enagritu otrzymanego z ługowania. Warstwy powierzchniowe próbek koncentratu enagritu badano przy pomocy spektroskopii XPS. Ługowanie mechanicznie aktywowanego enagritu z Na2S prowadzi do całkowitej ekstrakcji arsenu (zawartość As w suchej pozostałości po ługowaniu wynosi 0,06%), a następnie do dekompozycji enargitu Cu3AsS4 z utworzeniem nowych faz siarczku miedzi i jarosytu. Pomiary wykonane techniką spektroskopii XPS nie wykazały obecności arsenu w żadnej postaci w próbce otrzymanej po ługowaniu.