Impact and dynamic resistance of SFRCC modified by varied superplasticizers

The paper presents results of examinations of steel fiber reinforced cement composites (SFRCC) modified by superplasticizers based on different chemical substances. The described SFRCC were made on the basis of fine aggregate cement matrix modified by steel fibers of an aspect ratio l/d = 50. Fine aggregate matrix composed of waste aggregate (obtained during hydroclassification) was modified by an addition from 0% to 2.8% (by volume) of hooked steel fibers and 1% of superplasticizer. After establishing basic parameters of fresh mix and hardened fiber reinforced composites, the main tests were a drop-weight test of the SFRCC plates and dynamic harmonic loading of beams. Results achieved this way allowed to specify the influence of the specific superplasticizer on the behaviour of SFRCC subjected to a dynamic force.

---

W referacie przedstawiono wyniki badań nad fibrokompozytami cementowymi wykonanymi na bazie drobnych kruszyw odpadowych. Do wykonania fibrokompozytów wykorzystano włókna stalowe produkcji krajowej. Włókna dozowano w ilości od 0 do 2,8% (objętościowo). Badania obejmowały swym zakresem dwa etapy. Etap pierwszy stanowiły badania cech świeżej mieszanki (konsystencja) oraz badania stwardniałych fibrokompozytów wykonane w sposób statyczny (gęstość, wytrzymałość na ściskanie). Drugi etap stanowiły badania cech dynamicznych omawianych fibrokompozytów obejmujące swym zakresem badania uderzeniowe oraz badania przy obciążeniu harmonicznym. Badania przy obciążeniu harmonicznym prowadzono na polowym stanowisku laboratoryjnym przy wykorzystaniu próbek wielkowymiarowych o długości 2000 mm i przekroju 200 mm x 100 mm.