Microstructural and mechanical properties of gravity-die-cast A356 alloy inoculated with yttrium and Al-Ti-B grain refiner simultaneously

In the present work, the effect of inoculating yttrium and Al-5Ti-1B simultaneously on A356 aluminum alloy has been studied. Gravity die casting process is used to cast the ASTM tensile test specimens for analysis. In each experiment, the Ti and B contents were maintained constantly at 0.1 and 0.02 wt% respectively. The addition of yttrium was manipulated at the amount of 0, 0.1, 0.2, 0.3, 0.4 and 0.5 wt%. Microstructural characterization of the as-cast A356 alloy was investigated by means of optical microscope and its phases are detected by XRD. The mechanical properties tested are tensile strength and hardness. The inoculation of yttrium was found to enhance the grain refinement effect of Al-5Ti-1B grain refiner and improve the mechanical properties. The optimal weight percentage of yttrium was found to be 0.3. The grain refining efficiency of combining yttrium and Al-5Ti-1B on A356 aluminum alloy was mainly attributed to the heterogeneous nucleation of TiB2 and TiAl3 particles which were dispersed more evenly in the presence of yttrium and the grain growth restriction effected by the accumulation of Al-Y compound at grain boundaries.