Density and molar volume of Al-Li-Mg solid alloys

Using the dilatometric method the densities of the solid Al-Li-Mg alloys were measured for two constant values of t=0.85 and 0.95 and for li concentrations changing from 0 to 0.25 mole fraction. The experiments were carried out in the temperature ranges: 293-818K and 293-718K for t=0.05 and 0.15, respectively. The temerature dependences of density were described by the parabolic equation of the form y=a+bT+cT2. The parameters a, b and c were calculated using the least squares method. It was found that the density isoterms for t=0.95 show slight nagative from the linear behaviour, while for t=0.85 an almost linear change is observed when plotting the density from Al-Mg alloys to pure Li density. The molar volume isotherms of Al-Li-Mg solid alloys calculated at the same temperatures as for the density are characterised by slow decreasing with the increase of Li content, except that calculated at 700K for t=0.85 showing an opposite trend.

---

Stosując metodę dylatometryczną zmierzono gęstość stopów Al-Li-Mg dla stopów charakteryzujących się stałym stosunkiem aluminium do magnezu wynoszącym 0.95 oraz 0.85. Pomiary prowadzono dla stopów, w których stężenie litu zmieniało się od 0 do 0.25 ułamka molowego oraz w zakresie temperatur od 293-818K dla t=0.95 oraz od 293-718 dla t=0.85. Zmiany gęstości z temeraturą zostały opisane zależnościami parabolicznymi postaci y=a+bT+cT2 a parametry a, b i c zostały wyliczone metodą najmniejszych kwadratów. Obliczone izotermy gęstości w 293K oraz 800K dla t=0.95 oraz w 293K dla t=0.85 charakteryzują się słabym ujemnym odstępstwem od zmiany liniowej między gęstością stopu dwuskładnikowego Al-Mg i gęstością Li.Natomiast, wyznaczone w tych samych temperaturach izotermy objętości molowej pokazują nieznaczny spadek z zawartościa litu z wyjatkiem izotermy dla T=700K oraz t=0.85, która charakteryzuje się bardzo słabą wzrostową tendencją.