Changes in the structure and strengthening of aged CuNi13Sn5 alloy induced by microadditions

The decomposition of saturated solid solution of CuNi13Sn5 alloy during ageing is presented. Decomposition of the solution leads to the formation of cellular precipitates of discontinuous transition. Formation of these precipitates is responsible for the fact that the alloy does not acquire appropriately high mechanical properties. Introduction of microadditions in the form of Si or Ti into CuNi13Sn5 alloy changed the precipitation kinetics. Si and Ti microadditions formed phases which decorated the grain boundaries, preventing nucleation and the subsequent migration of cellular precipitates of discontinuous transition. Elimination of cellular precipitates was responsible for the fact that CuNi13Sn5 alloy attained very great strength and plastic properties.

---

W pracy niniejszej przedstawiono rozpad przesyconego roztworu stałego stopu CuNi13Sn5 podczas starzenia. Rozpad roztworu doprowadza do powstania komórkowych wydzieleń przemiany nieciagłej. Powstanie tych wydzieleń jest przyczyną nie osiagania przez stop odpowiednio duzych własności mechanicznych. Wprowadzenie do stopu CuNi13Sn5 mikrododatków w postaci Si lub Ti zmieniło kinetykę wydzielania. Mikrododatki Si i Ti utworzyły fazy, które udekorowały granice ziaren, uniemozliwiając zarodkowanie a następnie migrację wydzieleń komórkowych przemiany nieciągłej. eliminacja wydzieleń komórkowych spowodowała, ze stop CuNi13Sn5 osiagnął bardzo duże własności wytrzymałościowe jak i plastyczne.