Calorimetric studies of the enthalpies of formation of NiTi2, NiTi and Ni3Ti

Solution calorimetry operated with the liquid Al bath have been used for the determination of enthalpies of formation of intermetallic compounds of the Ni-Ti system. These are needed for extensive studies on the quaternary system Al-Fe-Ni-Ti within the COST 535 program on advanced aluminides. At first, there were obtained enthalpies of solution of Ni and Ti in liquid Al amounting respectively: -150 0:4 (kJ/g.atom) for Ni and -128.8 ± 0.7 (kJ/g.atom) for Ti. Using these values of enthalpies of solution, the following values of enthalpies of formation were obtained: -25.3 ± 1.7 (kJ/mol of atoms) for NiTi2, -31.1 ± 1.1 (kJ/mol of atoms] for NiTi and -43.8 ± 1.6 (kJ/mol of atoms) for Ni3 Ti, respectively. The resulting values are in good agreement with literature data, both experimental and from theoretical calculations.

---

Technika kalorymetryczna (rozpuszczanie w ciekłym aluminium) została zastosowana do wyznaczania entalpii tworzenia związków międzymetalicznych z układu Ni-Ti. Dane te są potrzebne do badań układu czteroskładnikowego Al-Fe-Ni-Ti w ramach programu COST 535. W pierwszym etapie, wyznaczono entalpię rozpuszczania niklu i tytanu w ciekłym Al wynoszące -150 ± 0.4 (kJ/g.atom) dla Ni i -128.8 ± 0.7 (kJ/g.atom) dla Ti. Uzywając tych danych entalpii rozpuszczania, otrzymano następujące wartości entalpii tworzenia: -25.3 ± 1.7 (kJ/mol of atoms) dla NiTi2, -31.1 ± 1.1 (kJ/mol of atoms) dla NiTi i -43.8 ± 1.6 (kJ/mol of atoms) dla Ni3 Ti. Otrzymane wartości są w dobrej zgodności z danymi literaturowymi.