Microstructure and tensile properties of sand cast and die cast AE44 magnesium alloy

The AE44 magnesium alloy was prepared by gravity and die casting methods. The microstructure and mechanical properties were investigated. The results demonstrated that microstructure of sand casting consist of Iarge grains of a solid solution and needle-shaped Al11RE3 phase, globular particles of Al10RE2Mn7 and smali volume fraction of Al2RE. Die casting process caused significant refinement of structure and change of phase composition. Die cast AE44 alloy consists of Al11RE3 phase and precipitates of Al2RE and Al2.12RE0.88 compounds. The mechanical properties at room and elevated temperaturę of the sand cast alloy are relatively Iow due to coarse-grain structure. Die-casting process increases the ultimate tensile strength, yield strength and elongation of AE44 magnesium alloy.

---

W pracy przedstawiono wyniki badań mikrostruktury i właściwości mechanicznych stopu magnezu AE44 po odlewaniu do formy piaskowej i ciśnieniowym. Mikrostrukturę odlewu piaskowego charakteryzuje znaczna gruboziarnistość i obecność faz międzymetalicznych AI11RE3, Al10RE2Mn7 i Al2RE, której udział objętościowy jest nieznaczny. Zastosowanie odlewania ciśnieniowego powoduje silne rozdrobnienie mikrostruktury i zmiany składu fazowego. W odlewie ciśnieniowym obserwuje się iglastą fazę AI11RE3 oraz wydzielenia faz A12RE i Al2.12RE0.88- Właściwości mechaniczne odlewu piaskowego w temperaturze otoczenia i podwyższonej są stosunkowo niskie. Po odlewaniu ciśnieniowym obserwuje się podwyższenie wytrzymałości na rozciąganie, granicy plastyczności oraz wydłużenia.