The study of corrosion behaviour of stainless steels L904 (0,05C, 1,5Mn, 0,27Si, 0,21Cr, 25,1Ni, 4,4Mo, 1,6Cu) and A211 (0,07C, 2,0Mn, 5,0Si, 18,5Cr, 21Ni, 1,2Mo) were performed in pure concentrated sulfuric acid (96% H2SO4, at 90°C) and in the presence of potasium fluoride impurities (5ppm and 10ppm F-). The following techniques were used in the study: linear sweep voltammetry (LSV), chronoamerometry, complimented by scanning electron spectroscopy (SEM) and X-ray photoelectron spectroscopy (XPS) analysis. These kinds of steel are extensively used as structural materials in chemical processing and production of sulfuric acid. Corrosion resistance of these steels depend on alloying elements (presence of silicon) and structure of surface layer.
Przeprowadzono badania korozyjne stali chromowo – niklowych, L904 (0,05C, 1,5Mn, 0,27Si, 0,21Cr, 25,1Ni, 4,4Mo, 1,6Cu) i A211 (0,07C, 2,0Mn, 5,0Si, 18,5Cr, 21Ni, 1,2Mo) w czystym stężonym kwasie siarkowym (96% H2SO4, przy temperaturze 90°C) oraz w kwasie zanieczyszczonym fluorkiem potasu (5ppm i 10ppm F-). Stosowano elektrochemiczne techniki polaryzacyjne (woltamperometryczne i chronoamperometryczne) uzupełnione analizą powierzchni przy pomocy metod spektroskopowych, skaningowej spektroskopii elektronowej (SEM) oraz rentgenowskiej spektroskopii fotoelektronów (XPS). Stale te stosowane są jako materiały konstrukcyjne na urządzenia w procesie produkcji kwasu siarkowego. Odporność korozyjna stali zależy od dodatków stopowych (głównie obecności krzemu) i budowy warstwy pasywnej.