The influence of high temperature plastic deformation on magnetic properties of Ni2MnGa type single crystals

The work presents experimental results on the influence of high temperature plastic deformation on the magnetic properties of Ni2MnGa type single crystals. It has been shown that room temperature plasticity of the Ni2MnGa single crystals is limited to very small strains (lower than 10-2), whereas at 1073K these single crystals could be plastically compressed to strains greater than 5x10-1. Magnetic properties of deformed and undeformed samples have been studied in low and high magnetic field. The analysis of the obtained magnetic hysteresis at different temperatures indicate a significant impact of the plastic deformation on the coercive field and the remanent magnetization (an increase by a factor of 3) and a lack of the effect on the saturation magnetization.

---

W pracy przedstawiono wyniki doświadczalne dotyczące wpływu wysokotemperaturowej deformacji plastycznej na własności magnetyczne monokryształów typu Ni2MnGa. Wykazano, iż plastyczność badanych monokryształów Ni2MnGa w temperaturze otoczenia jest ograniczona do bardzo małych odkształceń, nie większych niż 10-2, natomiast w 1073K badane monokryształy można ściskać do odkształceń wiekszych niż 5x10-1. Przeprowadzono badania własności magnetycznych w małym oraz w dużym polu na próbkach przed i po procesie wysokotemperaturowego ściskania. Analiza pętli histerezy magnetycznej uzyskanych przy różnych temperaturach wskazuje na istotny wpływ odkształcenia plastycznego na zwiększenie wartości pola koercji oraz namagnesowania resztkowego (około trzykrotne) i jego brak na wartość namagnesowania nasycenia.