Effect of Heat Treatment and Hydrostatic Extrusion on Mechanical Properties of a CuCrZr Alloy

In this work the effects of heat treatment and hydrostatic extrusion on mechanical properties of a CuCrZr alloy were investigated. The samples of CuCrZr alloy were subjected to solution annealing at a temperaturę of 1000°C for lh followed by water ąuenching. This was followed by aging at temperatures of 350, 450, 480, 550 and 650° C for the time raging from V2, to 3 hours. Two samples: (1) solution annealed and water ąuenched and (2) solution annealed, water ąuenched and aged at 480°C for 2 hours were subjected to the process of hydrostatic extrusion. The results obtained show that ageing increases the yield strength of the alloy by 500% whereas plastic deformation by hydrostatic extrusion by 1000%. The synergic effects of precipitation and deformation strengthening were also observed on samples subjected to ageing prior to or after hydrostatic extrusion. However, it is suggested that the two strengthening mechanisms are not fully additive.

---

W pracy badano wpływ obróbki cieplnej i wyciskania hydrostatycznego na właściwości mechaniczne stopu CuCrZr. Próbki ze stopu CuCrZr poddano przesycaniu z temperatury 1000°C w wodzie. Następnie były one starzone w temperaturze 350, 450, 480, 550 i 650°C w czasie od 1/2 do 3 godzin. Dwie próbki: (1) przesycana i (2) starzona w temperaturze 480°C przez 2 godziny zostały poddane procesowi wyciskania hydrostatycznego. Uzyskane wyniki wskazują, że starzenie powoduje wzrost plastyczności stopu o 500%, podczas gdy po odkształceniu plastycznym metodą wyciskania hydrostatycznego wzrasta o 1000%. Synergiczny efekt umocnienia wydzieleniowego i odkształceniowego zaobserwowano w próbkach poddanych starzeniu zarówno przed jak i po wyciskaniu hydrostatycznym. Uzyskane wyniki wskazują jednak, że obydwa mechanizmy umocnienia nie są w pełni addytywne.