The purpose of these iiwestigations was to obtain well-dispersed, unviscous ceramic slurries with zirconia nanopowder as solid phase and monosaccharides as dispersants. The as-obtained slurries should have high solid phase concentration and should be of Iow viscosity, just to be easily processed for example in slip casting process. High concentration of solid phase results in dense, strength products with desirable microstructure. In the research two different zirconia nanopowders were ńwestigated - the first, with an average particie size of 17nm (CEREL) and the latter, with an average particie size of 44nm (Inframat Advanced Materials). Rheological properties of ceramic slurries were tested.

---

Celem przeprowadzonych badań było otrzymanie dobrze upłynnionych ceramicznych mas lejnych zawierających nanopro-szek dwutlenku cyrkonu jako fazę stałą i wodny roztwór cukru prostego, D-fruktozy, jako substancję upłynniającą. Pożądanymi właściwościami tak uzyskanych mas powinno być m.in. wysokie stężenie fazy stałej i względnie niska lepkość, która ułatwiałaby formowanie elementów z tychże mas. Dzięki wysokiemu stężeniu fazy stałej, możliwe byłoby zaś, otrzymanie dobrze zagęszczonych produktów o odpowiedniej wytrzymałości mechanicznej i pożądanej mikrostrukturze. W przedstawionych badaniach użyto dwóch nanoproszków ZrC>2 - proszku o średniej wielkości ziarna 17nm, firmy CEREL, (Boguchwała, Polska), i proszku o średniej wielkości ziarna 44nm, firmy Inframat Advanced Materials, (Farmington, USA). Przedmiotem artykułu były badania reologiczne ceramicznych mas lejnych zawierających wymienione proszki oraz dodatek D-fruktozy w postaci wodnego roztworu.