Analytical electron microscopy of lamellar precipitates in AlZnTi alloys

A technique of analytical electron microscopy was used in order to determine the changes of chemistry of the phases formed in the microstructure of the Zn-25 wt.% Al cast alloy modified with Ti. The presence of the Ti(AI, Zn)3 compound was detected as well as two kinds of lamellar structures of the a and beta-phases having different partitioning of Al and Zn and various amount of Ti. It was suggested that the first kind of lamellar precipitates was formed during monotectoid transformation at the conditions far away from the equilibrium state while the second kind was a result of a discontinuous precipitation beginning after a longer cooling time of casting Titanium appeared only within the alpha and beta lamellae of monotectoid and it came from the Ti gradient adjacent to the Ti(AI. Zn), compound. Therefore, the amount of Ti decreased along increasing distance from the compound.

---

Metodą analitycznej mikroskopii elektronowej dokonano oceny zmian składu chemicznego faz występujących w mikrostrukturze stopu odlewniczego Zn-25 wag.% Al po modyfikacji tytanem. Stwierdzono występowanie wydzieleń bogatych w Ti, a identyfikowanych jako Ti(Al, Zn), oraz dwóch rodzajów struktury płytkowej faz alfa i beta, różniących się proporcjami Al i Zn, a także zawartością Ti. Przedstawiono hipotezę, że pierwszy typ wydzieleń płytkowych powstaje podczas przemiany monotektoidalnej stopu w warunkach dalekich od stanu równowagi, podczas gdy drugi jest wynikiem wydzielania nieciągłego, zaczynającego się po dłuższym okresie stygnięcia odlewu. Ti występuje jedynie w płytkach faz alfa i beta monotektoidu i pochodzi z gradientu tego pierwiastka istniejącego wokół Ti (Al, Zn)3, dlatego też ilość Ti w płytkach maleje w miarę wzrostu odległości od tych wydzieleń.