Identification of the Si-F bonds and phase composition of selected slags from the CaO-SiO2-CaF2 system using infrared spectroscopy

The CaO-SiO2-CaF2 phase system was investigated for selected slags using infrared spectroscopy. Si-O, Si-O(Si) and Si-F bonds were found in the slags and the type of occurring phases and chemical compounds was determined. The Si-F type bonds occurred only a larger content of CaF2. Using the examination results, the stages of the reaction of formation of the SiF4 gaseous phase were proposed. An important role has been found to be played by Si-F bonds that initiate two stages of the reaction of formation of the SiF4 gaseous phase. In the slags containing 4.02% and 9.887c of CaF2 no Si-F bonds were identified.

---

Badano układ fazowy CaO-SiO2-CaF2 dla wybranych żużli przy użyciu spektroskopii w podczerwieni. Opisano układ żużlowy CaO-SiO2-CaF2 oraz metodykę badawczą. Stwierdzono wiązania Si-O, Si-O(Si) i Si-F w badanych żużlach oraz określono rodzaj występujących faz i związków chemicznych. Wiązania typu Si-F występowały tylko przy większej zawartości CaF2. Wykorzystując wyniki badań zaproponowano etapy zachodzącej reakcji tworzenia się fazy gazowej SiF4. Stwierdzono istotną rolę wiązań Si-F, które inicjują dwa etapy reakcji tworzenia gazowej fazy SiF4. W żużlach zawierających 4.02% i 9.88% CaF2 nie stwierdzono wiązań Si-F.