Influence of strain path on microstructure and texture changes during deformation and recrystallization of Al single crystals with orientation (110)[001]

Al single crystals with the orientation (110) [001] were cold rolled (true strains 0.51 and 0.92) and subsequently compressed in a channel die in such a way that the new direction of plastic flow was parallel to the former transverse rolling direction and the compressed surface was parallel to the rolling plane. The microstructurc after rolling was uniform. The channel die compression brought about a rotation of the initial orientation around the ND (the rotation angle increased with deformation to about 28°). Distribution of earliest recrystallized grains was essentially random and after completion of recrystallization the grains were large. The recry stall ization textures are formed according to the oriented growth theory.

---

Monokryształy Al o orientacji (110) [001] walcowano (nadając odkształcenia rzeczywiste 0,51 i 0,92), a następnie ściskano w matrycy z kanałem w ten sposób, by nowy kierunek plastycznego płynięcia był równoległy do kierunku poprzecznego podczas walcowania, zaś ściskana płaszczyzna była równoległa do płaszczyzny walcowania. Po przewalcowaniu monokryształy charakteryzowały się stosunkowo jednorodną mikrostrukturą. Ściskanie w matrycy z kanałem powodowało obrót orientacji wokół KN (kąt obrotu orientacji zwiększał się z odkształceniem do około 28°). Rozmieszczenie pierwszych zrekrystalizowanych ziaren było względnie losowe, a po zakończeniu rekrystalizacji ziarna były duże. Tekstury rekrystalizacji tworzone były zgodnie z teorią uprzywilejowanego wzrostu.