Application of accelerated test ASTM C 1260 to aggregate containing calcium carbonate

The reactive aggregate containing calcium carbonate was tested according to ASTM C1260. At 80°C NaOH reacts with calcium carbonate with formation of calcium hydroxide and sodium carbonate. Independently of this reaction mortars of cements with addition of fly ash or slag present drasticly lower expansion in the range of non reactive aggregate. Cement matrix in these mortars adsorbs much more sodium than in CEM I mortar. Simultaneously in case of fly ash or slag silica grains in aggregate are influenced principaly by calcium ions and on their surface C-S-H is formed. Sodium silicate in these mortars contains also much more calcium which probably decreases its swelling.

---

Zbadano reaktywne kruszywo zawierające węglan wapniowy metodą ASTM C1260. W 80°C NaOH reaguje z węglanem wapniowym z utworzeniem wodorotlenku wapnia i węglanu sodowego. Niezależnie od tej reakcji zaprawy z cementów zawierających dodatek popiołu lotnego lub żużla granulowanego wykazują znacznie mniejszą ekspansję w zakresie wyznaczonym dla niereaktywnego kruszywa. Matryca cementowa w tych zaprawach adsorbuje znacznie więcej sodu niż w zaprawie z CEM l. Równocześnie w przypadku popiołu lotnego lub żużla na ziarna krzemionki w kruszywie działają głównie jony wapniowe w wyniku czego powstaje na ich powierzchni faza C-S-H. Także utworzony żel krzemianu sodowego zawiera znacznie więcej wapnia co prawdopodobnie zmniejsza jego pęcznienie.