Wpływ stabilizatorów na hydratację Beta-C2S

The effect of stabilizers, added as 0.5% by mole, on the Beta-C2S hydration process was investigated. The hydraulic activity of Beta-C2S with stabilizers was related to results for Beta-C2S stabilized by thermal treatment. The hydration of dicalcium silicate doped with Ba2+ added as 1 and 3% (by mole) was also studied. The experiments were carried out at room temperature on the pastes produced at w/c ratio 0.5, as well as on the suspensions with l/s ratio 100 or 200. The accelerating effect of Ba2+ introduced to the Beta-C2S structure was found as well as the retardation of the hydration process in the samples stabilized with As5+, B3+, Cr6+, P5+ and V5+ ions.

---

Dokonano oceny wpływu na hydratację Beta-C2S szeregu stabilizatorów, które wprowadzono do krzemianu dwuwapniowego w ilości 0,5% mol. i porównano ją z aktywnością hydrauliczną Beta-C2S uzyskanego na drodze stabilizacji termicznej. Przedmiotem badań była również hydratacja krzemianu dwuwapniowego zawierającego 1 i 3% mol Ba2+. Hydratację prowadzono w temperaturze pokojowej w zaczynach, w których stosunek masy wody do masy Beta-C2S (l/s) = 0,5 oraz w zawiesinach wodnych o stosunku l/s =100 lub 200. Stwierdzono, że wprowadzenie do struktury Beta-C2S jonów Ba2+ przyspiesza hydratację krzemianu dwuwapniowego, podczas gdy jony As5+, B3+, Cr6+, P5+ i V5+ opóźniają postęp hydratacji Beta-C2S.