Influence of protons on oxide compounds applied in optoelectronic devices

Changes in optical properties of some oxide compounds (YAG, YAG: Nd³⁺, YAG: Ce³⁺, YAG: Ce³⁺, Mg²⁺, YAG: Cr³⁺, YAG: Cr⁴⁺, SrLaGa₃O₇: Dy³⁺, SrLaGa₃O₇: Cr³⁺, SrGdGa₃O₇:Cr³⁺ and LiNbO₃: Cu²⁺) induced by 21 MeV proton irradiation were studied. In the optical absorption spectra lines which belong to optically active dopants (like Ce³⁺, Cr³⁺, Fe³⁺) and F-type color centers are seen. Influence of proton irradiation on such centers is observed. It seems to be attributed to the ionization and/or recombination of definite centers. Moreover, for relatively high proton fluencies, Frenkel defects are probably created.

---

Badano zmiany właściwości optycznych materiałów tlenkowych (YAG, YAG: Nd²⁺, YAG: Ce²⁺, YAG: Ce²⁺, Mg²⁺, YAG: Cr²⁺, YAG: Cr ⁴⁺ , SrLaGa₃O₇: Dy²⁺, SrLaGa₃O₇: Cr²⁺, SrGdGa₃O₇:Cr²⁺ oraz LiNbO₃: Cu²⁺) indukowane przez wiązkę protonów o energii 21MeV z cyklotronu. Wśród linii absorpcyjnych obserwowano linie należące do domieszek aktywnych (jak Ce²⁺, Cr²⁺, Fe²⁺) oraz do centrów barwnych typu F. Oddziaływanie protonów na te centra wydaje się być związane z jonizacją i/lub rekombinacją powyższych centrów. Ponadto, dla względnie wysokich strumieni protonów (1014 protonów/cm²), obserwuje się powstawanie defektów Frenkla.